| 1. | Scn are excellent stripping agents
Scn也有很好的反萃作用。 |
| 2. | Development of new anti - stripping agent based on adhesion of asphalt with aggregate
基于沥青与集料界面粘附性的抗剥落剂的开发 |
| 3. | The anti stripping performance is significant improved by using cement and anti - stripping agent together
在联合使用时，安山岩集料沥青混凝土的抗水损害能力提高显著。 |
| 4. | Inorganic additives is better than organic anti - stripping agent in terms of the effect of short and long term ageing
在短、长期使用效果方面,无机添加剂效果明显好于有机抗剥落剂。 |
| 5. | It can be concluded from the experimental results that both cement and anti - stripping agent show improvement on moisture stability of asphalt concrete
结果表明，水泥和抗剥落剂均可以提高沥青混凝土抗水损害能力。 |
| 6. | Long term immersing marshall test and frozen - thaw cycle test were used to investigate the anti - stripping performance of andesite asphalt mixture using cement and anti - stripping agent
摘要采取长时间浸水马歇尔试验和多循环冻融劈裂试验方法，对掺加了水泥、抗剥落剂的安山岩集料沥青混凝土水稳定性能进行研究。 |
| 7. | Au radioactive tracer method . the effect of several variables such as stripping agent concentrations , the volume ratio of stripping agents to gold loaded organic phase and the continuous extraction after stripping was studied under 20 . it is found that nh
等对季铵盐载金有机相的反萃，考察了反萃剂的浓度有机相与反萃剂的体积比等对反萃率的影响。 |
| 8. | Are excellent stripping agents for both n - octanol and tbp system . the organic phase can be rebirth by kcl aqueous solution . the stripping efficiency was agreement with perchloride effect . the effect of cosolvent on the stripping percentage was also discussed
在较高浓度时都是很好的反萃剂，反萃效率符合高氯酸盐效应，反萃后有机相具备连续萃取的能力。 |
| 9. | The paper analyzed the mechanism of the early moisture damage on the basis of survey , had carried out a series of laboratory tests to study the prevention measures from three aspects , that were gradation of the surface course and compaction capacity and the anti - stripping performance of hydrated lime qua anti - stripping agent
本文在调查的基础上，通过分析沥青路面早期水损害产生的机理，从沥青路面表面层级配、压实性能和以消石灰作为抗剥落剂的抗剥落性能三方面对沥青路面早期水损害进行了大量的室内试验研究。 |
| 10. | The results showed that the gradation , which designed by volumetric methods , has perfect water - stability and other pavement performance also can meet the demands of expressway . by integrating compaction capacity and pavement performances , the optimal ratio of the structural layer thickness to the maximum particle - size is 2 . 5 . the water resistance of the mixture added amine type anti - stripping agent attenuates severely after long - term aging , but the mixture added hydrated lime not only can improve obviously the capacity of water resistance , but also has perfect long - term pavement performance
研究结果表明，采用体积法设计的级配不仅具有较好的水稳定性而且其它路用性能均满足高速公路面层的要求；综合考虑压实性能及路用性能，提出了沥青路面表面层结构层厚度与混合料最大粒径的合理比例为2 . 5 ；掺有液体胺类抗剥落剂的沥青混合料经长期老化后其抗水损害能力衰减严重，而掺加消石灰的混合料能显著提高其抗水损害能力，且长期性能较好，是一种优良的抗剥落剂。 |